ATI Grade 12

UNS R53400

Product Documents

Data Sheet English (PDF)

Product Specifications By Form

Bar

Composition

Element	Minimum (weight %)	Maximum (weight %)	Typical (weight %)
Ni	0.6	0.9
Mo	0.2	0.4
Fe		0.30
O		0.25
C		0.08
N		0.03
H		0.015
Ti	Balance

Density

lb/in³	g/cm³
0.163	4.51

Tensile Strength

ksi	MPa
70 min	483 min

Yield Strength

ksi	MPa
50 min	345 min

Elongation

18% min

Billet

Composition

Element	Minimum (weight %)	Maximum (weight %)	Typical (weight %)
Ni	0.6	0.9
Mo	0.2	0.4
Fe		0.30
O		0.25
C		0.08
N		0.03
H		0.015
Ti	Balance

Density

lb/in³	g/cm³
0.163	4.51

Tensile Strength

ksi	MPa
70 min	483 min

Yield Strength

ksi	MPa
50 min	345 min

Elongation

18% min

Specifications

ASTM B265, ASME SB-265

Plate

Composition

Element	Minimum (weight %)	Maximum (weight %)	Typical (weight %)
Ni	0.6	0.9
Mo	0.2	0.4
Fe		0.30
O		0.25
C		0.08
N		0.03
H		0.015
Ti	Balance

Density

lb/in³	g/cm³
0.163	4.51

Tensile Strength

ksi	MPa
70 min	483 min

Yield Strength

ksi	MPa
50 min	345 min

Elongation

18% min

Specifications

ASTM B265, ASME SB-265

Sheet

Composition

Element	Minimum (weight %)	Maximum (weight %)	Typical (weight %)
Ni	0.6	0.9
Mo	0.2	0.4
Fe		0.30
O		0.25
C		0.08
N		0.03
H		0.015
Ti	Balance

Density

lb/in³	g/cm³
0.163	4.51

Tensile Strength

ksi	MPa
70 min	483 min

Yield Strength

ksi	MPa
50 min	345 min

Elongation

18% min

Specifications

ASTM B265, ASME SB-265

Strip

Composition

Element	Minimum (weight %)	Maximum (weight %)	Typical (weight %)
Ni	0.6	0.9
Mo	0.2	0.4
Fe		0.30
O		0.25
C		0.08
N		0.03
H		0.015
Ti	Balance

Density

lb/in³	g/cm³
0.163	4.51

Tensile Strength

ksi	MPa
70 min	483 min

Yield Strength

ksi	MPa
50 min	345 min

Elongation

18% min

Specifications

ASTM B265, ASME SB-265

Contact

Contact