ATI 6-7™


UNS R56700


Product Documents

Documents

Product Specifications By Form

Bar

Metallurgical Condition 1,300°F anneal. 0.2% Yield Strength. Reduction in Area, 25%.

Composition

ElementMinimum (weight %)Maximum (weight %)Typical (weight %)
Ta 0.5 
O 0.20 
C 0.08 
H 0.009 
Nb7.0  
Al6.0  
Fe0.15  
N0.03  
TiBalance  

Density

lb/in3g/cm3
0.1634.51

Tensile Strength

ksiMPa
125 min862 min

Yield Strength

ksiMPa
115 min793 min

Hardness

32 HRC max

Elongation

10% min
Billet

Metallurgical Condition 1,300°F anneal. 0.2% Yield Strength. Reduction in Area, 25%.

Composition

ElementMinimum (weight %)Maximum (weight %)Typical (weight %)
Ta 0.5 
O 0.20 
C 0.08 
H 0.009 
Nb7.0  
Al6.0  
Fe0.15  
N0.03  
TiBalance  

Density

lb/in3g/cm3
0.1634.51

Tensile Strength

ksiMPa
125 min862 min

Yield Strength

ksiMPa
115 min793 min

Hardness

32 HRC max

Elongation

10% min