ATI 6-2-4-2^™

UNS R54620 & R54621

Product Documents

Data Sheet English (PDF)

Product Specifications By Form

Bar

Metallurgical Condition 1,800°F anneal, Elongation 15%, Reduction in Area 30%

Composition

Element	Minimum (weight %)	Maximum (weight %)	Typical (weight %)
C		0.10
H		0.015
Al	6.0
Zr	4.0
Sn	2.0
Mo	2.0
O	0.2
Fe	0.05
N	0.04
Ti	Balance

Density

lb/in³	g/cm³
0.164	4.54

Tensile Strength

ksi	MPa
150 min	1035 min

Yield Strength

ksi	MPa
140 min	966 min

Hardness

28 HRC max

Elongation

15% min

Specifications

MIL T-9047G

Billet

Metallurgical Condition 1,800°F anneal, Elongation 15% , Reduction in Area 30%

Composition

Element	Minimum (weight %)	Maximum (weight %)	Typical (weight %)
C		0.10
H		0.015
Al	6.0
Zr	4.0
Sn	2.0
Mo	2.0
O	0.2
Fe	0.05
N	0.04
Ti	Balance

Density

lb/in³	g/cm³
0.164	4.54

Tensile Strength

ksi	MPa
150 min	1035 min

Yield Strength

ksi	MPa
140 min	966 min

Hardness

28 HRC max

Elongation

15% min

Specifications

MIL T-9047G