ATI 15Mo™


UNS R58150


Product Documents

Documents

Product Specifications By Form

Bar

Metallurgical Condition 1,475°F anneal. 0.2% Yield Strength. Reduction in Area, 60%.

Composition

ElementMinimum (weight %)Maximum (weight %)Typical (weight %)
C 0.05 
H 0.015 
Mo15.0  
O0.15  
Fe0.1  
N0.01  
TiBalance  

Density

lb/in3g/cm3
0.1794.95

Tensile Strength

ksiMPa
115 min793 min

Yield Strength

ksiMPa
95 min655 min

Hardness

24 HRC max

Elongation

22% min
Billet

Metallurgical Condition 1,475°F anneal. 0.2% Yield Strength. Reduction in Area, 60%.

Composition

ElementMinimum (weight %)Maximum (weight %)Typical (weight %)
C 0.05 
H 0.015 
Mo15.0  
O0.15  
Fe0.1  
N0.01  
TiBalance  

Density

lb/in3g/cm3
0.1794.95

Tensile Strength

ksiMPa
115 min793 min

Yield Strength

ksiMPa
95 min655 min

Hardness

24 HRC max

Elongation

22% min