ATI K-500™ Nickel-Based Alloy


UNS N05500


Product Documents

Documents

Product Specifications By Form

Bar

Composition

ElementMinimum (weight %)Maximum (weight %)Typical (weight %)
Cu2733 
Al2.303.15 
Fe 2.0 
Mn 1.5 
Ti0.350.85 
Si 0.50 
C 0.18 
S 0.01 
Ni63.0  

Density

lb/in3g/cm3
0.3068.45

Tensile Strength

ksiMPa
130 min896 min

Yield Strength

ksiMPa
85 min586 min

Hardness

27 HRB max

Elongation

20% min

Specifications

AMS 4676, ASTM F 467, F 468

Billet

Composition

ElementMinimum (weight %)Maximum (weight %)Typical (weight %)
Cu2733 
Al2.303.15 
Fe 2.0 
Mn 1.5 
Ti0.350.85 
Si 0.50 
C 0.18 
S 0.01 
Ni63.0  

Density

lb/in3g/cm3
0.3068.45

Tensile Strength

ksiMPa
130 min896 min

Yield Strength

ksiMPa
85 min586 min

Hardness

27 HRB max

Elongation

20% min

Specifications

AMS 4676, ASTM F 467, F 468

Plate

ATI K-500™ Alloy is typically supplied in the solution annealed condition with a hardness of 185 HBW max. The mechanical properties of material precipitation heat treated according to QQ-N-286 are shown below.


Composition

ElementMinimum (weight %)Maximum (weight %)Typical (weight %)
Cu2733 
Al2.303.15 
Fe 2.0 
Mn 1.5 
Ti0.350.85 
Si 0.50 
Co 0.25 
C 0.18 
Zn 0.02 
P 0.02 
Pb 0.006 
Sn 0.006 
S 0.006 
Ni63.0  

Density

lb/in3g/cm3
0.3068.45

Tensile Strength

ksiMPa
130 min896 min

Yield Strength

ksiMPa
80 min552 min

Elongation

20% min

Specifications

QQ-N-286 Form 6